Monoblanco

[Leeroy]

Hi guys, hope everyone happy , I'm spraying Parex monoblanco Tuesday and never sprayed this. Now I'm told it's different to most of the other mono I've sprayed. Has anyone sprayed this and how do you get on with it thanks

 

[plasterjfe]

Its loose. Too wet or too heavy it can slide. Just do a small panel first u be right. After that its nice

 

[Jgreenplastering]

Not sprayed it but handballed many a time and it's some of the nicest in my opinion.
@keithuk
@bobby
@Rigsby
@owls
@HLRexteriors
These guys to name a few can prob tell you what it's like to spray.


Sent from my iPhone using Tapatalk

 

[plasterjfe]

Its not like their monorex by the way

 

[Leeroy]

Thanks guys, I'm lucky in this case because it's only 4 gable tops 15m2 in each. So a good practice with this stuff, I was told it wets up, so don't play with it

 

[Leeroy]

Also would you go with overnight scrape or accelerator with this stuff cheers

 

[plasterjfe]

Overnights at these temps. What u sprayin over

Sent from my LG-D855 using Tapatalk

 

[User___removed]

Never used it but heard it can be a pain to spray
Good luck mate

 

[Leeroy]

Overnights at these temps. What u sprayin over

Sent from my LG-D855 using Tapatalk

Over micro mate

 

[Leeroy]

Never used it but heard it can be a pain to spray
Good luck mate

Cheers mate I've heard the same

 

[plasterjfe]

Over micro at 15 mm be sweet overnight. Can u justify the measure over 2 days tho price wise?

Sent from my LG-D855 using Tapatalk

 

[craigcousinsde]

I find it slumps a bit. Got to get the consistency right. it doesn't like thickness

 

[Leeroy]

Over micro at 15 mm be sweet overnight. Can u justify the measure over 2 days tho price wise?

Sent from my LG-D855 using Tapatalk

Cheers mate,yeah it's no bother as in on the inside too 14 flats, so will work better cheers

 

[Leeroy]

I find it slumps a bit. Got to get the consistency right. it doesn't like thickness

So I hear mate never doing white again if it's s**t. Stick to thin coat haha

 

[Leeroy]

So what is the right consistency,not too wet not too stiff haha

 

[Rossi46]

Are you doing it with the Eze Lee?

 

[plasterjfe]

So what is the right consistency,not too wet not too stiff haha

If too wet slides. If too stiff u gotta rule/trowel it too hardnit will slide. U need to find the "sweet spot" then its loverly.
Dont worry just use the force

Sent from my LG-D855 using Tapatalk

 

[Leeroy]

If too wet slides. If too stiff u gotta rule/trowel it too hardnit will slide. U need to find the "sweet spot" then its loverly.
Dont worry just use the force

Sent from my LG-D855 using Tapatalk

Haha brilliant mate, I never normally worry. I normally adapt to product I've not used very quickly but there's a few lads telling me it's awful stuff . Cheers mate

 

[Leeroy]

Are you doing it with the Eze Lee?

Yes mate, the eze all the Parex is on the top floor already on the inside so will take the eze up on top floor and mix in there jobs a Good en

 

[plasterjfe]

Haha brilliant mate, I never normally worry. I normally adapt to product I've not used very quickly but there's a few lads telling me it's awful stuff . Cheers mate

I get asked to go on with gangs all the time and start em off with it. Think a few have moaned about the product to the suppliers. Job u got is ideal first use. Careful not to second pass too soon tho it can be tempting on a small measure but this wont take it

Sent from my LG-D855 using Tapatalk

 

[keithuk]

I get asked to go on with gangs all the time and start em off with it. Think a few have moaned about the product to the suppliers. Job u got is ideal first use. Careful not to second pass too soon tho it can be tempting on a small measure but this wont take it

Sent from my LG-D855 using Tapatalk

I always think your help and support with renders is one of the best on here ,Respect mate

 

[HLR External Renders]

Has a nice fine texture this stuff, I would spray the 15mtrs then have a play with it.

 

[plasterjfe]

I always think your help and support with renders is one of the best on here ,Respect mate

I guess the main reason of the forum is for fellow teadesmen to bounce ideas/advice round each other.

Some topics i dont agree with but mostly its all good keith

Sent from my LG-D855 using Tapatalk

 

[Wezly]

The stuffs dreadful if your not careful with it, don't play with it to much on the rule or it will start to run. It's a heavy, dense material, also a quicker set than monorex so bear that in mind.

We put 22 pallets of the stuff on one build a few years back, you soon get the jist of it.

 

[Rigsby]

Sounds like it is definately a two pass material.

 

[Leeroy]

I get asked to go on with gangs all the time and start em off with it. Think a few have moaned about the product to the suppliers. Job u got is ideal first use. Careful not to second pass too soon tho it can be tempting on a small measure but this wont take it

Sent from my LG-D855 using Tapatalk

Cheers mate appreciated advise [emoji106]

 

[Leeroy]

The stuffs dreadful if your not careful with it, don't play with it to much on the rule or it will start to run. It's a heavy, dense material, also a quicker set than monorex so bear that in mind.

We put 22 pallets of the stuff on one build a few years back, you soon get the jist of it.

Will do cheers mate

 

[Leeroy]

Sounds like it is definately a two pass material.

Yes john, I'm gonna first pass mesh, hopefully this will stop the slumping, then second pass mate [emoji106]

 

[Rigsby]

Sounds like Jubs ocr on Vezecryil. Rush it and it slides off, play withi it and it slides.

 

[User___removed]

I always think your help and support with renders is one of the best on here ,Respect mate

Without a doubt
Your up there mind Keith for me

 

[Andy M]

So with these reports it's as bad as blanc during littoral then?.

 

[Andy M]

Du littoral lol

 

[SpankySouthport]

Think it's the same product just renamed

 

[plasterjfe]

So with these reports it's as bad as blanc during littoral then?.

No its not as tricky as blanc. Its an improvement on it but still has some of its characteristics. Its kind of half way between that and mono.

Sent from my LG-D855 using Tapatalk

 

[Leeroy]

Hi guys did the monoblanco this week it went good once I took the advise on board, I sprayed two gable one and meshed then sprayed second pass. It is funny stuff it doesn't like been sprayed too thick or it runs, you can't hit it too quick with the serrated edge or it runs, you can't Spatz it too quick or it runs lol,as been said you have to get the sweet spot with it all, so thanks everyone [emoji106] appreciated